  • 产品名称:CX-AED368-150 type acrylic low-temperature curing anodic electrophoretic paint
  • 产品型号:
  • 所属分类:
  • 材质:
  • 表面处理:
  • 在线咨询
产品详情 / Detail

1.Product Overview
CX-AED368-150 type acrylic low-temperature cured anode electrophoretic paint (new product) is the energy-saving, eco-friendly and lead-free electrophoretic paint with international quality independently developed by Caixin company. It is the color electrophoretic paint developed for the fields of aluminum/ magnesium alloy profiles, electrical appliances and hardware coating in China.
The product of this model has the following features:
1.Low curing temperature, up to 150 CX30min
2.The appearance of the coating film is smooth with good luster and high transparency
3.Super uniform electrophoretic ability, easy for adjusting the tank liquid
4.The tank liquid has good stability, with coating flow, it doesn’t need special technology, and it is easy for paint management;
5.The paint features high coating efficiency, economic, with waste water discharge, green and eco-friendly
6.The coating film has high hardness and strong corrosion resistance with excellent performance
7.It is suitable for both transparent glossy electrophoretic paint and various color electrophoretic paints with colorful paste, and the color is elegant and natural
? 2.Product quality index
CX-AED368-150coating film quality index

Testing Items

Varnish (transparent)

Test conditions

Appearance

Smooth without blemish

Visual inspection

Glossiness(60%)

≥90

Vanceometer

Coating film hardness(H)

4-5

GB/T6739

Cross cut test for adhesion ( 1mm grid)

100/100

GB/T9286

Salt spray resistance24h,CASS(R)

≥9.5

GB/T10125

Hydrochloric acid resistance

Without air bubbles and other obvious changes after test

GB/T5237.3

Alkali resistance 24 hours(R)

≥9.5

GB/T5237.3

Washing resistance

Without air bubbles, peeling and other obvious changes on the composite film after test

GB/T5237.3

Boiling water resistance

Without air bubbles, crack, crease, peeling and color change on the coating film after test

GB/T5237.3

3.Packaging and Storage
1.Package: 25L or 200L plastic barrel
Storage: During storage, the product shall be kept ventilated and dry without direct sunlight, keep it far from heat and fire source, prevent ice under low temperature in winter. The storage period is 6 months from the production date under 0 - 30℃.Products exceeding shelf life shall be determined by experiments whether it should be put into use